| Particle Size | 2.2-2.6mm |
|---|---|
| Specific Surface Area | ≥850 M2/g |
| Purity | ≥99% |
| Carrier Material | Alumina |
| Boiling Point | Not Available |
| Pore Volume | 0.6-0.8 Cm3/g |
|---|---|
| Na2O Content | ≤0.2% |
| Surface Area | 100-110 M2/g |
| Crystalline Phase | Q-Al2O3 |
| Moisture Content | ≤1% |
| Material del portador | de aluminio |
|---|---|
| Application | Catalyst For 2-ethylanthraquinone Hydrogenation |
| Specific Surface Area | ≥850 M2/g |
| Boiling Point | Not Available |
| Purity | ≥99% |
| Color | Blanco |
|---|---|
| Crushing Strength | ≥80N |
| Cao Content | ≤0.05% |
| Chemical Composition | Al2O3 ≥ 97% |
| Size | 1-5mm |
| Contenido del MgO | ≤ 0,05% |
|---|---|
| Contenido de humedad | el ≤1% |
| Apariencia | Polvo blanco |
| Contenido de Cao | ≤ 0,05% |
| Contenido SiO2 | ≤ 0,05% |
| Fase cristalina | Se trata de una mezcla de las siguientes sustancias: |
|---|---|
| Área de superficie | 100 a 110 m2/g |
| Estabilidad térmica | Hasta 1200℃ |
| Tamaño de las partículas | 1.6-1.8 mm |
| Contenido de Na2O | ≤ 0,2% |
| Tamaño de las partículas | 2.2-2.6 mm |
|---|---|
| Almacenamiento | Conservar en un lugar seco |
| Material del portador | de aluminio |
| La pureza | ≥99% |
| Aplicación | Catalizador para la hidrogenación de 2-etilantraquinona |
| Contenido del MgO | ≤ 0,05% |
|---|---|
| Área de superficie | 100 a 110 m2/g |
| Apariencia | Polvo blanco |
| Densidad de volumen | 0.6-0.65 G/cm3 |
| Contenido Fe2O3 | ≤0.02% |
| Volumen de los poros | 0.6-0.8 Cm3/g |
|---|---|
| Formulación química | Al2O3 |
| Contenido SiO2 | ≤ 0,05% |
| Estabilidad térmica | Hasta 1200℃ |
| Contenido de Cao | ≤ 0,05% |
| Superficie específica | ≥ 850 M2/g |
|---|---|
| Almacenamiento | Conservar en un lugar seco |
| Punto de ebullición | No está disponible |
| Tamaño de las partículas | 2.2-2.6 mm |
| Material del portador | de aluminio |